Structural, mechanical and tribological properties of NbCN-Ag nanocomposite films deposited by reactive magnetron sputtering.

Abstract

spectroscopy (EDS), X-ray diffraction (XRD), field emission scanning electron microscope (FE-SEM), high resolution transmission electron microscopy (HRTEM), Raman spectrometry, nano-indentation, and high-temperature sliding wear tests. Results indicated that face-centered cubic (fcc) NbN, hexagonal close-packed (hcp) NbN and fcc Ag, amorphous C and amorphous CNx phase co-existed in the as-deposited NbCN-Ag films. After doping with 2.0 at.% Ag, the hardness and elastic modulus reached a maximum value of 33 GPa and 340 GPa, respectively. Tribological properties were enhanced by adding Ag in NbCN-Ag films at room temperature. When the test temperature rose from 300 to 500 °C, the addition of Ag was found beneficial for the friction properties, showing a lowest friction coefficient of ~0.35 for NbCN-12.9 at.% Ag films at 500 °C. This was mainly attributed to the existence of AgOx, NbOx, and AgNbOx lubrication phases that acted as solid lubricants to modify the wear mechanism.